| Marsnite (MB) series are alumina
fused cast refractories whereby highly pure alumina raw material is melted at
over 2000°C and poured into a mold. |
| MB-G |
| The MB-G consist of approximately 50% α
-alumina and 50% ß -alumina, where intertwined crystals of both materials
result in a very dense structure. Under 1300°C, it has a corrosion resistance
against molten glass that equals Zirconite, and shows excellent performance against
contamination to molten glass, that it is very suitable for paving blocks and
forehearth channel blocks. |
| MB-U |
| The MB-U refractory comprises of 100% ß
-alumina, which shows extremely high resistance to alkaline vapor. Moreover, the
intersected texture of large ß-alumina shows significant resistance against
spalling. MB-U refractory is suitable for superstructure where batch scattering
is not a problem. |
| MB-A |
| The MB-A is a fused cast refractory of over
90% α -alumina. It shows excellent stability under high temperatures. Their
crystal structure is completely stable and dense, it is hard, slag erosion resistant
and abrasion resistant. It shows high performance for high temperature tunnel
kiln interior lining and carbon furnace interior lining. |
|
|