HOME > Data bank > Monolithic refractories > Other Monolithic refractories > Mortar Monolithic refractories   Other Monolithic refractories Mortar Product Corhart Mortar High alumina mortar Fireclay mortar Basic mortar CMS CM-15 OM-SK36 OM-SK35 OM-SK34 MGM MGM-15C MMC 20000 ECM-F MEM Chemical composition(%) SiO2 25 2.8 33 39 48 6.3 45 .0 6.2 6.0 6.2 Al2O3 70 96.0 62 54 47 1.3 1.5 5.7 14.2 7.8 Fe2O3 1.8 0.1 2.0 3.1 1.7 0.4 0.3 3.0 7.1 - Cr2O3 - - - - - - - 6.0 17.6 8.8 TiO2 1.9 - 1.0 1.8 1.8 tr. tr. tr. - - CaO 0.2 - 0.4 0.4 0.2 1.1 1.0 1.3 0.8 - MgO 0.3 - 0.4 0.4 0.1 90.1 75.1 76.5 51.3 71               14.7 (Fixed carbon)       Refractoriness(SK) >37 >42 >36 >35 >34 >40 >40 >40 >40 >40 Package 25kg packed in a bag Airset Mortar Product Tight seal TMA TMN Types Fused mullite Chamotte Refractoriness(SK) 37 32 Max operating temperature 1,600 1,450 Chemical composition(%) SiO2 25 52 Al2O3 67 40 Fe2O3 1.5 3.0 Cr2O3 - - MgO - - Adhesion strength (kg/cm2) 100°C3hrs. 20 20 900°C  3hrs. 20 25 1200°C 3hrs. 25 25 1400°C 3hrs. 25 30 Condition D W D W Powder Slurry Powder Slurry Package 25kg packed in a bag 30kg packed in a bag 25kg packed in a bag 30kg packed in a bag CM-8-3Mortar Product CM-8-3 Chemical composition(%) SiO2 7 Al2O3 86 Binder addition(%) (28.0) Installation Water retention time(m-s) 2-30 Water retention time(m-s) 1-30  Properties Adhesive strength at RT(kg/cm2) Dried 55 1000°Cx3hrs. 50 1200°Cx3hrs. 60 1400°Cx3hrs. 70 Adhesive strength at elevated temperature(kg/cm2) at 1200°C > 45 at 1400°C > 20 Package 25kg packed in a bag or 25kg packed in a can with a separate bonding agent >> Mortar To page top