| Product |
LC-12T |
LC-11 |
LC-10 |
LC-10S |
LC-10N |
LC-7 |
LC-RMG |
| Max operating temperature(°C) |
1350 |
1200 |
1200 |
1200 |
1100 |
900 |
1100 |
| Fill factor(t/m3) |
1.10 |
1.00 |
0.70 |
0.80 |
0.70 |
0.35 |
1.20 |
| Water additions(wt%) |
35 - 45 |
30 - 40 |
70 - 85 |
60 - 75 |
45 - 65 |
80 - 110 |
30 - 40 |
| Chemical composition(%) |
SiO2 |
38 |
37 |
42 |
39 |
40 |
46 |
49 |
| Al2O3 |
42 |
41 |
32 |
33 |
15 |
11 |
28 |
| Bulk specific gravity |
110°Cx24hrs. |
1.20 |
1.10 |
0.75 |
0.85 |
0.75 |
0.40 |
1.30 |
| ( )Temp.x3hrs. |
1.10
(1200) |
1.00
(1000) |
0.65
(1000) |
0.65
(1000) |
0.70
(1000) |
0.35
(700) |
1.23
(900) |
Compressive strength
( )Bending strength
(MPa) |
110°Cx24hrs. |
5
(1.5) |
5
(1.5) |
1.5
(0.4) |
2.5
(0.7) |
2.0
(1.0) |
0.6
(0.2) |
5
(2.0) |
| 600°Cx3hrs. |
4
(1.2) |
|
|
|
|
0.4
(0.1) |
3
(1.0) |
| 800°Cx3hrs. |
|
|
|
|
|
|
|
| 900°Cx3hrs. |
4
(1.2) |
|
|
|
|
|
3
(1.0) |
| 1000°Cx3hrs. |
|
2.5
(1.0) |
1.5
(0.8) |
3
(1.0) |
1
(0.5) |
|
|
| 1200°Cx3hrs. |
4
(1.2) |
|
|
|
|
|
3
(1.0) |
| 1400°Cx3hrs. |
|
|
|
|
|
|
|
| Premanent linear change(%) |
( )Temp.x3hrs. |
-0.8
(1200) |
-0.3
(1000) |
-1.3
(1000) |
-1.3
(1000) |
-1.4
(1000) |
-1.2
(700) |
-0.5
(900) |
| Thermal expansion(%) |
at( )Temp.°C |
|
|
|
|
|
|
0.1
(800) |
Thermal conductivity
(W/mK) |
at100°C |
0.30 |
0.30 |
0.17 |
0.17 |
0.17 |
0.11 |
0.35 |
| at400°C |
0.35 |
0.35 |
0.21 |
0.21 |
0.21 |
0.14 |
0.40 |
| at1000°C |
0.40 |
0.40 |
0.30 |
0.30 |
0.30 |
|
0.45 |
| Standard package quantity(kg) |
25 |
20 |
20 |
20 |
20 |
10 |
25 |
| Features |
Trowel application |
General purpose |
General purpose |
High strength |
General purpose |
High inslative performance |
General purpose |
| Typical applications |
Types of kilns |
Heating furnace |
Types of kilns |
Chimney,
Types of kilns |
Types of kilns |
Types of kilns |
Types of kilns |